hot-dip相关论文
以Cu93P钎料为基体,在其表面热浸镀锡,制备CuPSn钎料,采用扫描电镜、万能力学试验机、显微硬度计、差热分析仪、箱式电阻炉和体视......
采用一浴法对铜进行了热浸镀镀铝试验,热浸镀时间为8s,热浸镀温度为690~740℃。研究了热浸镀温度对Cu/Al复合材料组织、导电性能及......
在高强钢热浸镀铝硅合金中,通常会有一定量Mn溶解到镀液中,对镀层凝固组织产生影响。本文研究了热浸镀用Al-10Si-2Fe合金中Mn元素......
采用X射线衍射仪、扫描电子显微镜、能谱仪、透射电子显微镜、全浸腐蚀及中性盐雾腐蚀试验等方法，对比研究 Zn-0.5Al-1.5Mg、Zn-2Al......
Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa h
A C-Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s......
Lead and Cadmium Distribution in Tubes of Galvanized Steel by Hot-Dip Used for Drinking Water Supply
The main objective of this work was to evaluate the presence of lead and cadmium in galvanized steel tubes by hot-dip us......
Bottom dross obtained from zinc bath and the typical bottom dross defects on galvanized and galvannealed coating were me......
Based on the galvannealed phase transformation theory,the phase and powder level of a galvannealed coating produced on o......
在本研究中使用Zn-xAl合金液对铝合金表面进行热浸镀,重点研究不同Al含量的Zn-xAl合金液在坩埚中凝固的铸锭组织及在铝基体表面凝......
本文研究了Ce、Ti协同作用对热镀锌铝镀层组织和生长动力学的影响。通过控制Ce、Ti元素含量设计熔池成分,采用扫描电镜(SEM)和能谱......
为研究耐蚀性更高但生产成本与传统热镀锌成本相当的新镀层，制备了添加微量钛元素的热浸镀锌层，分别从表观质量、镀层厚度、电化学测......
研究了钢板热浸镀55A1-Zn-1．5Si合金层的工艺，分析了不同的助镀剂配方及浸镀参数对镀层质量的影响，确定出了较理想的热浸镀工艺。结果......
采用熔体处理和金属助镀相结合的新工艺在Q235钢表面先预镀一层锌后再进行热浸镀Al-43%Zn-1.6%Si合金;用光学显微镜、扫描电子显微......
...
对钢丝热浸镀Galfan合金镀层的开裂进行了研究。采用SEM、EDS、XRD、TEM、XPS分别分析了镀层的组织形貌、相组成及元素的结合方式，......
渗铝基本上是在上世纪末和本世纪初发展起来的一种化学热处理工艺, 它既可以提高基体材料的抗高温氧化性能, 还能提高基体材料在一......